6 inch solar cells with a length of 150 x 150 mm deliver 40 % more power than customary cells. |
| |
|
| |
Data sheet of 6 inch solar cells |
| |
|
Product
|
Multicrystalline silicon solar cell
|
|
Format
|
150mm× 150mm± 0.5mm |
|
Thickness
|
300um ± 40um |
|
Front (-)
|
2mm bus bars (silver) |
|
blue anti-reflection coating (Silicon nitride)
|
|
Back (+)
|
5 mm wide soldering pads (Silver/Aluminium) |
|
back surface field (Aluminium)
|
|
|
| |
|
| |
The typical value |
| |
|
Current at 0.5V
|
6.17~7.10A
|
|
Isc
|
6.97~7.42A |
|
Uoc
|
0.608~0.621V |
|
Pmax
|
3.11~3.51W |
|
Efficiency
|
13.8~15.6% |
|
| |
|
| |
All data at standard testing conditions:STC-1000W/m 2 , AM 1.5, 25 |
| |
|
Temperature coefficient power
|
-0.43%/K
|
|
Temperature coefficient current
|
+2.20mA/K |
|
Temperature coefficient voltage
|
-2.12mV/K |
|
| |
| |
 |
| |
|
|
5 inch solar cells with a length of 125 x 125 mm |
| |
|
| |
Data sheet of 5 inch solar cells |
| |
|
Product
|
Multicrystalline silicon solar cell
|
|
Format
|
125mm× 125mm± 0.5mm |
|
Thickness
|
300um ± 40um |
|
Front (-)
|
1.5mm bus bars (Silver) |
|
blue anti-reflection coating (Silicon nitride)
|
|
Back (+)
|
5mm wide soldering pads (Silver/Aluminium) |
|
back surface field (Aluminium)
|
|
| |
|
| |
The typical value |
| |
|
Current at 0.5V
|
3.95~4.93A
|
|
Isc
|
4.56~5.08A |
|
Uoc
|
0.590~0.6157V |
|
Pmax
|
1.89~2.53W |
|
Efficiency
|
12.00~16.24% |
|
| |
|
| |
All data at standard testing conditions:STC-1000W/m 2 , AM 1.5, 25 |
| |
|
Temperature coefficient power
|
-0.43%/K
|
|
Temperature coefficient current
|
+1.53mA/K |
|
Temperature coefficient voltage
|
-2.12mV/K |
|
| |
|
| |
 |
| |
|
|
4 inch solar cells with a length of 103 x 103 mm |
| |
|
| |
Data sheet of 6 inch solar cells |
| |
| Product |
Multicrystalline silicon solar cell |
| Format |
103mm× 103mm± 0.5mm |
| Thickness |
300um ± 40um or 260um ± 35 |
| Front (-) |
1.5mm bus bars (Silver) |
|
blue anti-reflection coating (Silicon nitride)
|
|
Back (+)
|
4.5mm wide soldering pads (Silver/Aluminium) |
|
back surface field (Aluminium)
|
|
| |
|
| |
The typical value |
| |
| Current at 0.5V |
1.26~1.47A
|
| Isc |
3.11~3.29A |
| Uoc |
0.594~0.608V |
| Pmax |
3.11~3.51W |
| Efficiency |
12~14.49% |
|
| |
|
| |
All data at standard testing conditions:STC-1000W/m 2 , AM 1.5, 25 |
|
Temperature coefficient power
|
-0.43%/K
|
|
Temperature coefficient current
|
+2.20mA/K |
|
Temperature coefficient voltage
|
-2.12mV/K |
|