Descriptions: Solder Coated,Flat Copper Wire |
| |
|
 |
CHEMISTRY |
| |
|
| |
Wire:CDA 110 (UNS C11000,ETP) per ASTM B49 with a 99.90% min copper content. |
| |
|
| |
|
|
| 60% Tin / 40% Lead 96.5% Tin / 3.5% Silver |
62% Tin / 36% Lead / 2% Silver |
| Sn:60% +1.5% / 5% Sn:Remainder |
Sn:61~63% |
| Pb:Balance(40%) Pb:0.10%max |
Ag:1~3% |
| Sb:5%max Sb:0.12%max |
Sb:0.5%max |
| As:0.025%max Ag:3.4~3.8% |
As:0.025max |
| Al:0.005%max Cu:0.08%max |
Al:0.005%max |
| Zn:0.005%max Cd:0.005%max |
Zn:0.005max |
| Bi:0.25%max Al:0.005%max |
Bi:0.25%max |
| Cd:0.001%max Bi:0.15%max |
Cd:0.001%max |
| Cu:0.08%max As:0.01%max |
Cu:0.08%max |
| Fe:0.02max |
Pb:Balance(36%) |
| Zn:0.005max |
= |
|
| |
|
|
MECHANICAL SPECIFICATIONS |
| |
|
| A) Tensile Strength Ranges (As tested prior to solder Coating) : |
| Annealed=206.8 to 275.8 Newtons / square mm(30,000 to 40,000 PSI) |
| 1/4Hard=275.8 to 344.7 Newtons / square mm(40,000 to 50,000 PSI) |
| 1/2Hard=317.2to 393 Newtons / square mm(46,000 to 57,000 PSI) |
|
| |
| |
B) Bare Copper Size Tolerances: |
| |
| Thickness |
| <0.254 mm(0.001) |
+/-0.0762 mm(+/-0.0003) |
| 0.254 mm(0.001) to 0.381 mm(0.015) |
+/-0.127 mm(+/-0.0005) |
| 0.381 mm(0.15) to 2.0321 mm(0.080) |
+/-0.254 mm(+/-0.001) |
| Width |
| <0.254 mm(0.001) |
+/-0.0762 mm(+/-0.003) |
| 2.54 mm(0.100) to 3081 mm(0.150) |
+/-0.127 mm(+/-0.005) |
| 3.81 mm(0.15) to 25.4 mm(1.000) |
+/-0.254 mm(+/-0.010) |
|
| |
|